Moreover,
the length of the unmachined region (L U) is equal to 0. Thus, the critical value of V stage is calculated to be half of V tip. Figure 2c,d shows the scratched states after two tip scanning cycles with the conditions of V stage < 0.5V tip and V stage > 0.5V tip, respectively, which will be described in detail as follows: (2) As shown in Figure 2c, when V stage is less than half of V tip, the two regions machined in the adjacent AFM scanning cycles have an overlapping machined region with a length (L O) expressed by Equation 3. If the V stage is small to a certain value, the two adjacent overlapping machined regions also can overlap with each other. As shown in Equation 4, the ratio of L O and L stage can be expressed as an integer (N) plus a fraction (a). BVD-523 concentration From the geometrical relationship, the lengths of the N + 1 and N + 2 times the overlapping machined region can be obtained by 3-deazaneplanocin A cost Equations 5 and 6, respectively. Through Equations 5 and 6, the period of the ladder Selleck Bafilomycin A1 nanostructure is calculated to be L stage. Figure 2e shows the schematic of the cross section of the machined groove with the typical condition of N = 0. L 1 and L 2 represent the lengths of the one and two times machined regions, respectively. h 1 and h 2 are the corresponding depths.
(3) (4) (5) (6) As shown in Figure 2d, when V stage is larger than half of V tip, the two regions machined in the adjacent AFM scanning cycles are nonoverlapping, which can cause a length of the unmachined region (L U) expressed by Equation 7. Through Equations 2 and 7, the period of the ladder nanostructure is also calculated to be L stage. Figure 2f shows the schematic of
the cross section of the machined groove in this condition. h 1 represents one-time machined depth. (7) The real pitch in scratching (Δ) in these two conditions mentioned above can be obtained by Equation 8: (8) (2) When V stage > V tip, as shown in Figure 3, the scratched state is different from the condition shown in Figure 2. Figure 3a,b shows the machined states of after one and two tip scanning cycles, respectively. Phosphoprotein phosphatase By considering the geometric relationship, as shown in Figure 3b, L C, L U, and Δ can be obtained by Equations 9, 10, and 11, respectively. The length of the unmachined region (L U) only depends on the displacement of the AFM tip in one scanning cycle. From Equations 9 and 10, the period of the ladder nanostructure is calculated to be L stage. Figure 3c shows the schematic of the cross section of the machined groove in this condition. h 1 represents the one-time machined depth. (9) (10) (11) Matching relations between V tip and V stage under the condition of the stage motion and the feed rate in the opposite direction In this condition as shown in Figures 4 and 5, the feeding direction is along the positive direction of x axis, and the moving direction of the high-precision stage is along the negative direction of x axis.
No related posts.